1 / 1
The main alloying elements of 8011 aluminum strip are silicon (Si) and iron (Fe), with a silicon content of 0.5 - 0.9% and an iron content of 0.6 - 1.0%. The remaining is mainly aluminum, along with trace amounts of other elements such as copper, magnesium, and manganese.
In the O temper (fully annealed), the tensile strength is 70 - 110 MPa, the yield strength is 30 - 50 MPa, and the elongation is 20 - 40%. These properties make it have good formability and ductility, which is conducive to the processing and manufacturing of pipes. The mechanical Properties.
Can be customized according to your special request too!
The thickness of 8011 aluminum strip for pipes is usually in the range of 0.1 -1.0 mm, and the width can be 10 - 300mm. For example, some common thicknesses are 0.21 mm with a tolerance of ±0.02 mm, and widths can range from 20 - 300 mm with a tolerance of ±0.2 mm.
The main alloying elements of 8011 aluminum strip are silicon (0.5 - 0.9%) and iron (0.6 - 1.0%), with the remainder being primarily aluminum, along with trace amounts of copper, magnesium, and manganese.
In the O temper (fully annealed), it has a tensile strength of 70 - 110 MPa, a yield strength of 30 - 50 MPa, and an elongation of 20 - 40%, which ensures excellent formability and ductility for pipe processing.
The standard thickness ranges from 0.1 to 1.0 mm, and the width is usually between 10 and 300 mm. Custom dimensions can be accommodated to meet specific requirements.
It offers outstanding formability for easy roll-forming, high corrosion resistance to extend service life, and excellent adhesion properties with polyethylene after proper chemical degreasing.
It must be stored in a dry, ventilated environment (humidity under 60%), stacked on clean pallets (not directly on the floor), and separated with protective layers to prevent surface damage, indentation, or oxidation.